Durostone® UPM S2
GFK-UP
Durostone® UPM S2 is a fiber-reinforced plastic with very high mechanical properties. This plastic spheric a defined flammability. The fiber reinforcement is carried out with a glass mat or glass fabric.
raspberry red, similar RAL 3027cream, similar RAL 9001
sheet
Characteristics
- Special vinyl ester (VE) resin matrix reinforced with a combination of an e-glass roving mat and fabric
- SMC high-pressure laminate
- High mechanical strength
- High dielectric strength
Variants
Technical Specifications Durostone® UPM S2 red
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 1,95 |
| Flexural strength 1)┴ | ISO 178 | MPa | 350 |
| Flexural strength 1)┴ +130°C | ISO 178 | MPa | 175 |
| Modulus of elasticity in flexion 1)┴ | ISO 178 | MPa | 18000 |
| Modulus of elasticity in flexion 1)┴ +130°C | ISO 178 | MPa | 12000 |
| Compressive strength ┴ | ISO 604 | MPa | 480 |
| Tensile strength II | ISO 527 | MPa | 220 |
| Impact strength II (Charpy) | ISO 179 | kJ / m2 | 200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Flammability | UL 94 | / | V0 / 5mm |
| Smoke density & toxicity, class | NF F 16-101 | / | F0 |
| Fire test, class | NF P 92-501 | / | M2 |
| Temperature index | IEC 60216 | T.I. | 155 |
| Insulation class | IEC 60085 | / | F |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (4mm thickness) | ISO 62 | % | 0,5 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Electric strength 90°C under oil ┴ | IEC 60243 | kV / mm | 12 |
| Electric strength 90°C under oil II | IEC 60243 | kV/25mm | 75 |
| Relative permittivity (50 Hz) | IEC 60250 | εr | 4 |
| Dielectric loss factor (50 Hz) | IEC 60250 | tan δ | 0,01 |
| Specific surface resistance | IEC 60093 | Ω | 1010 |
| Comparative tracking index | IEC 60112 | CTI | 600 |
Technical Specifications Durostone® UPM S2 white
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 1,95 |
| Flexural strength 1)┴ | ISO 178 | MPa | 350 |
| Flexural strength 1)┴ +130°C | ISO 178 | MPa | 175 |
| Modulus of elasticity in flexion 1)┴ | ISO 178 | MPa | 18000 |
| Modulus of elasticity in flexion 1)┴ +130°C | ISO 178 | MPa | 12000 |
| Compressive strength ┴ | ISO 604 | MPa | 480 |
| Tensile strength II | ISO 527 | MPa | 220 |
| Impact strength II (Charpy) | ISO 179 | kJ / m2 | 200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Flammability | UL 94 | / | V0 / 5mm |
| Smoke density & toxicity, class | NF F 16-101 | / | F0 |
| Fire test, class | NF P 92-501 | / | M2 |
| Temperature index | IEC 60216 | T.I. | 155 |
| Insulation class | IEC 60085 | / | F |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (4mm thickness) | ISO 62 | % | 0,5 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Electric strength 90°C under oil ┴ | IEC 60243 | kV / mm | 12 |
| Electric strength 90°C under oil II | IEC 60243 | kV/25mm | 75 |
| Relative permittivity (50 Hz) | IEC 60250 | εr | 4 |
| Dielectric loss factor (50 Hz) | IEC 60250 | tan δ | 0,01 |
| Specific surface resistance | IEC 60093 | Ω | 1010 |
| Comparative tracking index | IEC 60112 | CTI | 600 |