Glastherm® HT 250 M
GFK-EP
Glastherm® HT 250 M boasts very high compressive strength and is particularly resistant to heat. The heat insulation system is ideally suited to the thermal insulation of press moulds and enables the conservation of energy during the pressing process. The heat insulation system is mainly used in hydraulic wood, plastic and tyre presses. Glastherm® HT 250 M is free of asbestos and can be easily cut and adapted with standard metal tools. We recommend diamond cutters for relatively large jobs.
- Maximum continuous operation temperature: 250 °C (482 °F)
- Very high compressive strength: 445 MPa (at 200 °C)
- Good thermal insulation
sheet
Characteristics
- Fibre-reinforced composite material developed for applications in field of thermal insulation (max. continuous operating temperature 250°C)
- Low thermal conductivity
- High compressive strength
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 324088 | Glastherm® HT 250 M pressed | sheet | sheet | 2.000 x 1.100 x 15 (+/-1) mm | 2,000 mm | 1,100 mm | 15 mm |
Technical Specifications Glastherm® HT 250 M
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 2,0 |
| Flexural strength ┴ | ISO 178 | MPa | 300 |
| Modulus of elasticity in flexion ┴ | ISO 178 | MPa | 22000 |
| Compressive strength 1)┴ | ISO 604 | MPa | 600 |
| Compressive strength 1)┴ +200°C | ISO 604 | MPa | 445 |
| Tensile strength II | ISO 527 | MPa | 250 |
| Impact strength ┴ (Charpy) | ISO 179 | kJ / m2 | 150 |
| Splitting force II | DIN 53463 | N | 5000 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Thermal conductivity 2)┴ | W / (m * K) | ≈ 0,23 | |
| Coefficient of linear expansion II | TMA (Mettler) | 10-6 x K-1 | 10 - 15 |
| Max. continuous operating temperature | °C | 250 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (4mm thickness) | ISO 62 | % | 0,15 |