Polystone® P (Copolymer) PGX + UV-stabilized white
PP-C
white, similar RAL 9010
sheetwelding rod
Characteristics
- High mechanical strength
- Good weldability
- High chlorine and UV resistant
- UV-resistant
Industries
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 427037 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | sheet | sheet | white, similar RAL 9010 | 4.000 x 1.220 x 20 mm | 4,000 mm | 1,220 mm | 20 mm | ||
| No stock item (MOQ) | 444902 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 2.000 x 5 mm | 3,000 mm | 2,000 mm | 5 mm | ||
| No stock item (MOQ) | 444904 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | welding rod | welding rod | white, similar RAL 9010 | Ø 3 (+/-0,2) mm | 3 mm | ||||
| No stock item (MOQ) | 444905 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | welding rod | welding rod | white, similar RAL 9010 | Ø 4 (-0,3/+0,2) mm | 4 mm | ||||
| No stock item (MOQ) | 444906 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | welding rod | welding rod | white, similar RAL 9010 | B=6,1 (-0,4/+0) x 4 (-0,4/+0,1) mm | 6.1 mm | 4 mm | |||
| No stock item (MOQ) | 454042 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | welding rod | welding rod | white, similar RAL 9010 | B=5 (+/-0,3) x 3 (+/-0,3) mm | 5 mm | 3 mm | |||
| No stock item (MOQ) | 462754 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | sheet | sheet | white, similar RAL 9010 | 4.000 x 1.500 x 20 mm | 4,000 mm | 1,500 mm | 20 mm | ||
| No stock item (MOQ) | 471687 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | sheet | sheet | white, similar RAL 9010 | 4.000 x 2.000 x 12 mm | 4,000 mm | 2,000 mm | 12 mm | ||
| No stock item (MOQ) | 472928 | Polystone® P (Copolymer) PGX + UV-stabilized white extruded | welding rod | welding rod | white, similar RAL 9010 | B=5,7 (-0,5/+0,1) x 3,8 (-0,4/+0) mm | 5.7 mm | 3.8 mm |
Technical Specifications Polystone® P (Copolymer) PGX + UV-stabilized white
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 0,92 |
| Water absorption | DIN EN ISO 62 | % | 0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 24 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 1400 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | > 20 |
| Shore hardness | DIN EN ISO 868 | scale D | 69 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 162 – 167 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,20 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 - 190 |
| Service temperature, long term | Average | °C | -30 … 100 |
| Service temperature, short term (max.) | Average | °C | 150 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 85 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,5 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,00019 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | >1013 | |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | 40 |