SustaPEI GF 30 natural
PEI
natural
rod
Characteristics
- High heat deflection temperature
- Flame retardant
- Low smoke development
- High stiffness
- High tensile strength
- High hardness
- high dimensional stability under heat
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 696851 | SustaPEI GF 30 natural extruded | rod | rod | natural | Ø 80 x 3000 mm | 3 000 mm | 80 mm | |||
| No stock item (MOQ) | 697173 | SustaPEI GF 30 natural extruded | rod | rod | natural | Ø 80 x 1000 mm | 1 000 mm | 80 mm | |||
| No stock item (MOQ) | 700289 | SustaPEI GF 30 natural extruded | rod | rod | natural | Ø 110 x 1000 mm | 1 000 mm | 110 mm |
Technical Specifications SustaPEI GF 30 natural
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,51 |
| Water absorption | DIN EN ISO 62 | % | 0,4 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 / V0 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 120 |
| Elongation at break | DIN EN ISO 527 | % | 4 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 5000 |
| Shore hardness | DIN EN ISO 868 | scale D | 92 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | - |
| Glass transition temperature | ISO 11357-3 | °C | 217 |
| Service temperature, long term | Average | °C | -30 … 170 |
| Service temperature, short term (max.) | Average | °C | 210 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 210 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 3,3 | |
| Dielectric dissipation factor (50 Hz) | IEC 60250 | 0,0016 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1015 |
| Comparative tracking index | IEC 60112 | 150 | |
| Dielectric strength | IEC 60243 | kV / mm | 35 |