Polystone® P (Homopolymer) EHS grey
PP-H
grey, similar RAL 7032
sheetwelding rodprofile
Characteristics
- High rigidity
- Good weldability
- Corrosion resistant
- Heat resistant
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 374198 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 3.000 x 1.500 x 20 mm | 3 000 mm | 1 500 mm | 20 mm | ||
| No stock item (MOQ) | 374199 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 3.000 x 1.500 x 15 mm | 3 000 mm | 1 500 mm | 15 mm | ||
| No stock item (MOQ) | 380511 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 3.000 x 1.500 x 10 mm | 3 000 mm | 1 500 mm | 10 mm | ||
| No stock item (MOQ) | 407286 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 4.000 x 2.000 x 40 mm | 4 000 mm | 2 000 mm | 40 mm | ||
| No stock item (MOQ) | 434644 | Polystone® P (Homopolymer) EHS grey extruded | welding rod | welding rod | grey, similar RAL 7032 | Ø 4 (-0,3/+0,2) mm | 4 mm | ||||
| No stock item (MOQ) | 434721 | Polystone® P (Homopolymer) EHS grey extruded | welding rod | welding rod | grey, similar RAL 7032 | Ø 4 (-0,3/+0,2) mm | 4 mm | ||||
| No stock item (MOQ) | 434722 | Polystone® P (Homopolymer) EHS grey extruded | welding rod | welding rod | grey, similar RAL 7032 | Ø 5 (-0,4/+0,2) mm | 5 mm | ||||
| No stock item (MOQ) | 434728 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 3.000 x 2.000 x 50 mm | 3 000 mm | 2 000 mm | 50 mm | ||
| No stock item (MOQ) | 449112 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 2.000 x 1.000 x 6 mm | 2 000 mm | 1 000 mm | 6 mm | ||
| No stock item (MOQ) | 451164 | Polystone® P (Homopolymer) EHS grey extruded | Rectangular hollow section | Rectangular hollow section (H20) | grey, similar RAL 7032 | 5.000 x 50 x 50 x 4,5 mm | 5 000 mm | 50 mm | 4,5 mm | 50 mm | |
| No stock item (MOQ) | 451165 | Polystone® P (Homopolymer) EHS grey extruded | welding rod | welding rod | grey, similar RAL 7032 | Ø 3 (+/-0,2) mm | 3 mm | ||||
| No stock item (MOQ) | 451166 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 4.000 x 2.000 x 15 mm | 4 000 mm | 2 000 mm | 15 mm | ||
| No stock item (MOQ) | 451167 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 4.000 x 2.000 x 10 mm | 4 000 mm | 2 000 mm | 10 mm | ||
| No stock item (MOQ) | 452001 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 2.000 x 1.000 x 8 mm | 2 000 mm | 1 000 mm | 8 mm | ||
| No stock item (MOQ) | 452799 | Polystone® P (Homopolymer) EHS grey extruded | sheet | sheet | grey, similar RAL 7032 | 2.000 x 1.000 x 4 mm | 2 000 mm | 1 000 mm | 4 mm |
Technical Specifications Polystone® P (Homopolymer) EHS grey extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,90 |
| Water absorption | DIN EN ISO 62 | % | 0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >30 |
| Elongation at yield stress | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1500 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >4 |
| Shore hardness | DIN EN ISO 868 | scale D | >70 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 162 ... 167 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,20 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
| Service temperature, long term | Average | °C | 0 ... 120 |
| Service temperature, short term (max.) | Average | °C | 150 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 90 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,4 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,00019 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |
| Dielectric strength | IEC 60243 | kV / mm | >40 |
Technical Specifications Polystone® P (Homopolymer) EHS grey pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,90 |
| Water absorption | DIN EN ISO 62 | % | 0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >30 |
| Elongation at yield stress | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1500 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >4 |
| Shore hardness | DIN EN ISO 868 | scale D | >70 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 162 ... 167 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,20 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
| Service temperature, long term | Average | °C | 0 ... 120 |
| Service temperature, short term (max.) | Average | °C | 150 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 90 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,4 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,00019 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |
| Dielectric strength | IEC 60243 | kV / mm | >40 |