Glastherm® HT 200 is a heat insulation system with a high level of stability which is suitable for processes with a working temperature of up to 200 °C (392 °F). Glastherm® HT 200 was developed specially for plastic and zinc die-casting moulds. It has good thermal insulation, enabling rapid die heating-up processes and therefore rapid start-up of the machines. Glastherm® HT 200 is free of asbestos and can be easily cut and adapted with standard metal tools.
SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
---|---|---|---|---|---|---|---|---|---|---|---|
No stock item (MOQ) | 428269 | Glastherm® HT 200 pressed | sheet | sheet | 2.445 x 1.255 x 22 mm | 2,445 mm | 1,255 mm | 22 mm | |||
No stock item (MOQ) | 443422 | Glastherm® HT 200 pressed | sheet | sheet | 2.445 x 1.255 x 27 mm | 2,445 mm | 1,255 mm | 27 mm | |||
No stock item (MOQ) | 447666 | Glastherm® HT 200 pressed | sheet | sheet | 2.445 x 1.255 x 12 (+/-0,1) mm | 2,445 mm | 1,255 mm | 12 mm | |||
No stock item (MOQ) | 505348 | Glastherm® HT 200 pressed | machined part | machined part | 2.046 x 327,5 x 20 (+/-0,1) mm | 2,046 mm | 327.5 mm | 20 mm | |||
No stock item (MOQ) | 505352 | Glastherm® HT 200 pressed | machined part | machined part | 1.532,5 x 216 x 20 (+/-0,1) mm | 1,532.5 mm | 216 mm | 20 mm | |||
No stock item (MOQ) | 505354 | Glastherm® HT 200 pressed | machined part | machined part | 1.035 x 216 x 20 (+/-0,1) mm | 1,035 mm | 216 mm | 20 mm |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Density | ISO 1183 | g / cm3 | 1,9 |
Flexural strength ┴ | ISO 178 | MPa | 200 |
Modulus of elasticity in flexion ┴ | ISO 178 | MPa | 12000 |
Compressive strength 1)┴ | ISO 604 | MPa | 320 |
Compressive strength 1)┴ +200°C | ISO 604 | MPa | 230 |
Tensile strength II | ISO 527 | MPa | 120 |
Impact strength ┴ (Charpy) | ISO 179 | kJ / m2 | 100 |
Splitting force II | DIN 53463 | N | 2200 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Thermal conductivity 2)┴ | W / (m * K) | ≈ 0,3 | |
Coefficient of linear expansion II | TMA (Mettler) | 10-6 x K-1 | ≈ 20 |
Max. continuous operating temperature | °C | 200 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Water absorption (method 1) | ISO 62 | % | 0,1 |