With modern presses and precise tools we produce the most varied FRP components and pressed parts from SMC and BMC-polyester products. In the SMC technique, a combination of resin and fibres is cured in a mould under pressure and heat. The production method enables time savings, high reproducibility and a smooth surface. The process is particularly suitable for medium-sized series.
Dimensions
With our presses we are able to produce pressed parts with dimensions of 150 x 150 x 150 mm up to 2,200 x 1,600 x 1,200 mm.
Test Method | Unit | Guideline Value | |
---|---|---|---|
Standard Color | RAL 7035 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Flexural strength ┴ | ISO 178 | MPa | 170 |
Modulus of elasticity in flexion ┴ | ISO 178 | MPa | 11000 |
Compressive strength ┴ | ISO 604 | MPa | 220 |
Tensile strength II | ISO 527 | MPa | 100 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Flammability | IEC 60707 | / | VO/3mm |
Coefficient of linear expansion ┴ | TMA (Mettler) | 10-6 x K-1 | 55 to 65 |
Coefficient of linear expansion II | TMA (Mettler) | 10-6 x K-1 | 15 to 25 |
Temperature of deflection under load | IEC 893-2 | °C | >200 |
Thermal conductivity | ISO 8302 | W/m K | 0.3 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Glass content | ISO 11667 | % | 30 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Electric strength 90°C under oil ┴ | IEC 60243 | kV / mm | 12 |
Electric strength 90°C under oil II | IEC 60243 | kV/25mm | 75 |
Comparative tracking index | IEC 60112 | CTI | 600 |