Sustamid® 66 black
PA — PA 66
black
sheetrod
Characteristics
- High abrasion resistance
- High absorption of moisture of up to 2.7 % in standard atmosphere
- High tensile strength
- High hardness
- good adhesive properties
- Good weldability
- High continuous service temperature
- Good machinability
- Good sliding properties
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 729252 | Sustamid® 66 black extruded | sheet | sheet | black | 50 x 620 x 3000 mm | 3,000 mm | 620 mm | 50 mm | ||
| No stock item (MOQ) | 930530 | Sustamid® 66 black extruded | rod | rod | black | Ø 35 x 1000 mm | 1,000 mm | 35 mm | |||
| No stock item (MOQ) | 934840 | Sustamid® 66 black extruded | sheet | sheet | black | 16 x 620 x 3000 mm | 3,000 mm | 620 mm | 16 mm | ||
| No stock item (MOQ) | 934914 | Sustamid® 66 black extruded | sheet | sheet | black | 16 x 620 x 1000 mm | 1,000 mm | 620 mm | 16 mm | ||
| No stock item (MOQ) | 689182 | Sustamid® 66 black calendered | sheet | sheet | black | 4,76 x 1220 x 2440 mm | 2,440 mm | 1,220 mm | 4.76 mm | ||
| No stock item (MOQ) | 689183 | Sustamid® 66 black calendered | sheet | sheet | black | 3,18 x 1220 x 2440 mm | 2,440 mm | 1,220 mm | 3.18 mm | ||
| No stock item (MOQ) | 809803 | Sustamid® 66 black calendered | sheet | sheet | black | 6,35 x 1220 x 2440 mm | 2,440 mm | 1,220 mm | 6.35 mm | ||
| No stock item (MOQ) | 922878 | Sustamid® 66 black calendered | sheet | sheet | black | 2,3 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 2.3 mm |
Technical Specifications Sustamid® 66 black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,15 |
| Water absorption | DIN EN ISO 62 | % | 2,8 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 85 |
| Elongation at break | DIN EN ISO 527 | % | 50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3300 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 3 |
| Shore hardness | DIN EN ISO 868 | scale D | 83 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 260 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,23 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -30 … 95 |
| Service temperature, short term (max.) | Average | °C | 170 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 100 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 3,8 | |
| Dielectric dissipation factor (50 Hz) | IEC 60250 | 0,015 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1013 |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | 25 |