Matrox® is outstanding for its extremely low coefficient of friction and high wear resistance and so optimally meets requirements for the lining of silos and bunkers.
SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
---|---|---|---|---|---|---|---|---|---|---|---|
No stock item (MOQ) | 366185 | Matrox® SI 12 black pressed | sheet | sheet | black, similar RAL 9004 | 6.000 x 2.500 x 13 mm | 6,000 mm | 2,500 mm | 13 mm | ||
No stock item (MOQ) | 438047 | Matrox® SI 12 black pressed | sheet | sheet | black, similar RAL 9004 | 3.000 x 2.000 x 50 mm | 3,000 mm | 2,000 mm | 50 mm | ||
No stock item (MOQ) | 438451 | Matrox® SI 12 black pressed | sheet | sheet | black, similar RAL 9004 | 6.000 x 2.000 x 50 mm | 6,000 mm | 2,000 mm | 50 mm | ||
No stock item (MOQ) | 475548 | Matrox® SI 12 black pressed | sheet | sheet | black, similar RAL 9004 | 2.000 x 1.000 x 20 mm | 2,000 mm | 1,000 mm | 20 mm | ||
No stock item (MOQ) | 475600 | Matrox® SI 12 black pressed | sheet | sheet | black, similar RAL 9004 | 6.000 x 2.000 x 20 mm | 6,000 mm | 2,000 mm | 20 mm |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Density | DIN EN ISO 1183-1 | g / cm3 | >0,94 |
Water absorption | DIN EN ISO 62 | % | 0,01 |
Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
Molecular weight | - | 106 g/mol | ≥4 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Yield stress | DIN EN ISO 527 | MPa | >19 |
Elongation at break | DIN EN ISO 527 | % | >50 |
Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >700 |
Notched impact strength | DIN EN ISO 11542-2 | kJ / m2 | >70 |
Shore hardness | DIN EN ISO 868 | scale D | >63 |
Wear resistance | Sand-slurry | 125 | |
Sand Slurry | 1018 Steel=10 | ∼ 120 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
Service temperature, long term | Average | °C | -100 … 80 |
Service temperature, short term (max.) | Average | °C | 130 |
Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 79 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Dielectric constant | IEC 60250 | 2,3 | |
Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0004 | |
Comparative tracking index | IEC 60112 | 600 | |
Dielectric strength | IEC 60243 | kV / mm | >40 |