Polystone® M Slide + AST black

PE — PE-UHMW - PE 1000

Polystone^® M is an ultra-high molecular weight polyethylene (PE-UHMW/PE 1000) used to solve friction, wear and material flow problems in many industries. The material is characterized by excellent sliding properties, extreme wear resistance, high impact strength and very good resistance to chemicals and has established itself in technical applications. The material is available in various colors.

black, similar RAL 9005

profile

Characteristics

Very low coefficient of friction
High abrasion resistance
Antistatic
Self-lubricating
Very good noise absorbtion
UV-resistant

Industries

Variants

	SKU	Name	Type	Type	Color	Measurements	Length	Width	Thickness	Height
No stock item (MOQ)	418302	Polystone® M Slide + AST black extruded	C-profile	C-profile (R265)	black, similar RAL 9005	6.000 x 90 x 14,5 mm	6,000 mm	90 mm	3.5 mm	14.5 mm
No stock item (MOQ)	418304	Polystone® M Slide + AST black extruded	C-profile	C-profile (R227)	black, similar RAL 9005	6.000 x 50 x 14 mm	6,000 mm	50 mm	14 mm

Technical Specifications Polystone® M Slide + AST black

General properties

	Test Method	Unit	Guideline Value
Density	DIN EN ISO 1183-1	g / cm³	>0,95
Water absorption	DIN EN ISO 62	%	0,01
Flammability (Thickness 3 mm / 6 mm)	UL 94		HB
Molecular weight	-	10⁶ g/mol	∼ 9

Mechanical properties

	Test Method	Unit	Guideline Value
Yield stress	DIN EN ISO 527	MPa	>20
Elongation at break	DIN EN ISO 527	%	>50
Tensile modulus of elasticity	DIN EN ISO 527	MPa	>600
Notched impact strength	DIN EN ISO 11542	kJ / m²	>110
Shore hardness	DIN EN ISO 868	scale D	>60

Thermal properties

	Test Method	Unit	Guideline Value
Melting temperature	ISO 11357-3	°C	130 ... 135
Thermal conductivity	DIN 52612-1	W / (m * K)	0,40
Thermal capacity	DIN 52612	kJ / (kg * K)	1,90
Coefficient of linear thermal expansion	DIN 53752	10^-6 / K	150 ... 230
Service temperature, long term	Average	°C	-250 … 80
Service temperature, short term (max.)	Average	°C	130
Vicat softening temperature	DIN EN ISO 306, Vicat B	°C	79