SustaPEI blue
PEI
brilliant blue, similar RAL 5007
rod
Characteristics
- High stiffness even at high temperatures
- Low smoke development
- Good resistance against high energy radiation
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 806372 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 65 x 3000 mm | 3.000 mm | 65 mm | |||
| No stock item (MOQ) | 806373 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 65 x 1000 mm | 1.000 mm | 65 mm | |||
| No stock item (MOQ) | 806708 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 55 x 3000 mm | 3.000 mm | 55 mm | |||
| No stock item (MOQ) | 806864 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 85 x 1000 mm | 1.000 mm | 85 mm | |||
| No stock item (MOQ) | 807267 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 40 x 1000 mm | 1.000 mm | 40 mm | |||
| No stock item (MOQ) | 807268 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 40 x 3000 mm | 3.000 mm | 40 mm | |||
| No stock item (MOQ) | 920148 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 85 x 3000 mm | 3.000 mm | 85 mm |
Technical Specifications SustaPEI blue
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,27 |
| Water absorption | DIN EN ISO 62 | % | 0,5 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 / V0 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 110 |
| Elongation at break | DIN EN ISO 527 | % | 12 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3100 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 86 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | - |
| Glass transition temperature | ISO 11357-3 | °C | 217 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,24 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,10 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 45 |
| Service temperature, long term | Average | °C | -50 … 170 |
| Service temperature, short term (max.) | Average | °C | 210 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 3,2 | |
| Dielectric dissipation factor (50 Hz) | IEC 60250 | 0,0015 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1015 |
| Comparative tracking index | IEC 60112 | 150 | |
| Dielectric strength | IEC 60243 | kV / mm | 30 |