Polystone® G B 100 RC + GK black
PE — PE-HD (PE 100)
black, similar RAL 9005
sheet
Characteristics
- Very good stress cracking resistance
- Chemical resistance
- Suitable for contact with drinking water
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 294296 | Polystone® G B 100 RC + GK black extruded | sheet | sheet | black, similar RAL 9005 | 6.000 x 1.400 x 15 mm | 6.000 mm | 1.400 mm | 15 mm | ||
| No stock item (MOQ) | 294298 | Polystone® G B 100 RC + GK black extruded | sheet | sheet | black, similar RAL 9005 | 3.000 x 1.400 x 15 mm | 3.000 mm | 1.400 mm | 15 mm | ||
| No stock item (MOQ) | 373147 | Polystone® G B 100 RC + GK black extruded | sheet | sheet | black, similar RAL 9005 | 3.400 x 1.400 x 15 mm | 3.400 mm | 1.400 mm | 15 mm |
Technical Specifications Polystone® G B 100 RC + GK black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,96 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Non-toxicity | + | ||
| MRS classification | ISO TR 9080 | PE 100 | |
| Approval | DIBt | ||
| Melt Flow Rate (MFR 190/5) | DIN EN ISO 1133 | g / 10 min | 0,22 |
| Moulding Compound PE | DIN ISO 1872-1 | PE-EACH-50T003 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >23 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1100 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >16 |
| Shore hardness | DIN EN ISO 868 | scale D | 63 |
| FNCT (4.0 MPa, 2 % Arkopal N 100, 80 °C) | ISO 16770 | h | >8760 |
| Tensile Strength (23°C) | ASTM D1457 | N/mm² | 4 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -50 ... 80 |
| Service temperature, short term (max.) | Average | °C | 100 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 67 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,5 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0004 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | >1014 | |
| Comparative tracking index | IEC 60112 | 600 | |
| Arc resistance | IEC 60093 | degree | L4 (*) |
| Dielectric strength | IEC 60243 | kV / mm | 30 |