Durolight® S1
GFK-UP
Durolight® is a new developed insulating composite material especially designed to meet the thermal and mechanical requirements of load bearing supports. Durolight® is manufactured from a special formulation of selected synthetic resins in combination with high-strength glass reinforcements.
sheet
Characteristics
- Glass-reinforced thermoset SMC high-pressure laminate developed for applications at cryogenic temperatures
- Low thermal conductivity
- Low weight
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 411172 | Durolight® S1 pressed | sheet | sheet | 2.440 x 1.220 x 10 (+/-0,8) mm | 2.440 mm | 1.220 mm | 10 mm | |||
| No stock item (MOQ) | 411173 | Durolight® S1 pressed | sheet | sheet | 1.350 x 1.220 x 22 (+/-1,4) mm | 1.350 mm | 1.220 mm | 22 mm | |||
| No stock item (MOQ) | 411832 | Durolight® S1 pressed | sheet | sheet | 2.440 x 1.220 x 43 (+/-1,59) mm | 2.440 mm | 1.220 mm | 43 mm | |||
| No stock item (MOQ) | 411833 | Durolight® S1 pressed | sheet | sheet | 2.440 x 1.220 x 30 (+/-1,45) mm | 2.440 mm | 1.220 mm | 30 mm | |||
| No stock item (MOQ) | 440827 | Durolight® S1 pressed | sheet | sheet | 2.440 x 1.220 x 9 (+/-0,2) mm | 2.440 mm | 1.220 mm | 9 mm |
Technical Specifications Durolight® S1
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 1,3 |
| Flexural strength ┴ | ISO 178 | MPa | 130 |
| Modulus of elasticity in flexion ┴ | ISO 178 | MPa | 8000 |
| Compressive strength 1)┴ | ISO 604 | MPa | 250 |
| Tensile strength II | ISO 527 | MPa | 60 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Coefficient of linear expansion II | TMA (Mettler) | 10-6 x K-1 | 15 - 20 |
| Thermal conductivity ┴ RT | W / (m * K) | ≈ 0,22 | |
| Thermal conductivity ┴ -196 | W / (m * K) | ≈ 0,18 2) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (method 1) | ISO 62 | % | 0,2 |