Glastherm® HT 250 M
GFK-EP
Glastherm® HT 250 M boasts very high compressive strength and is particularly resistant to heat. The heat insulation system is ideally suited to the thermal insulation of press moulds and enables the conservation of energy during the pressing process. The heat insulation system is mainly used in hydraulic wood, plastic and tyre presses. Glastherm® HT 250 M is free of asbestos and can be easily cut and adapted with standard metal tools. We recommend diamond cutters for relatively large jobs.
- Maximum continuous operation temperature: 250 °C (482 °F)
- Very high compressive strength: 445 MPa (at 200 °C)
- Good thermal insulation
板
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫なし(MOQあり) | 324088 | Glastherm® HT 250 M pressed | 板 | 板 | 2.000 x 1.100 x 15 (+/-1) mm | 2,000 mm | 1,100 mm | 15 mm |
技術仕様書 Glastherm® HT 250 M
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | ISO 1183 | g / cm3 | 2,0 |
| 曲げ強度 ┴ | ISO 178 | MPa | 300 |
| たわみ荷重弾性係数┴ | ISO 178 | MPa | 22000 |
| 圧縮強度1)┴ | ISO 604 | MPa | 600 |
| 圧縮強度1)┴ +200°C | ISO 604 | MPa | 445 |
| 引張強度II | ISO 527 | MPa | 250 |
| 衝撃強度(シャルピー衝撃試験)┴ | ISO 179 | kJ / m2 | 150 |
| Splitting force II | DIN 53463 | N | 5000 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 熱伝導率2)┴ | W / (m * K) | ≈ 0,23 | |
| 線膨張係数 II | TMA (Mettler) | 10-6 x K-1 | 10 - 15 |
| 最高連続使用温度 | °C | 250 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 吸水率 (4mm厚) | ISO 62 | % | 0,15 |